SikaCoat Plus

SikaCoat Plus

MULTIPURPOSE HIGH FLEXIBLE ACRYLIC BASED, ALKALI RESISTANT LIQUID APPLIED MEMBRANE

One component multipurpose high flexible acrylic based, alkali resistant liquid applied membrane. It can be applied on parapet walls, external walls, etc.

  • Alkali resistant.
  • Reduce construction times.
  • Easy application.
  • Excellent hiding power.
  • High elasticity.
  • Excellent UV stability.
  • Impermeable.
  • Crack bridging ability.
  • Can be diluted with 10% water (we only recommend for priming).
  • Low consumption.
Product Data Sheet Show all documents

Usage

  • SikaCoat Plus used for new plastering*
  • Finishing
  • Sealing joints, laps and roofing screws on various kind of roofs (roof tile, asbestos, zinc)
  • Parapet walls
  • External walls
* After 3 days cured with moisture < 25 % and pH < 11.  

Advantages

  • Alkali resistant.
  • Reduce construction times.
  • Easy application.
  • Excellent hiding power.
  • High elasticity.
  • Excellent UV stability.
  • Impermeable.
  • Crack bridging ability.
  • Can be diluted with 10% water (we only recommend for priming).
  • Low consumption.

Packaging

20 kg, 4 kg pail

Colour

Grey, Stone Grey, White, Latte.

Product Details

Product Information

Chemical base

Aqueous Acrylic Dispersion

Shelf life

12 months from date of production.

Storage conditions

Stored properly in original, unopened and undamaged sealed packaging in dry conditions at temperatures between +5 °C and +30 °C and protect from direct sunlight.

Density

~1.3 ± 0.05 kg/L (at +30 °C)
System information

System Structure

Without Membrane System (DFT ~200 micron) :

First coat

: 1 x SikaCoat Plus

Second coat: 1 x SikaCoat Plus
Technical Information

Tensile Strength

> 1.0 N/mm2 (without membrane)

(ASTM D412: 2006a (2013))

Adhesion in Peel

> 1.0 N/mm2 (without membrane)

Application

Application Information

Ambient Air Temperature

< 35 °C

Substrate Temperature

< 35 °C

Drying time

> 3 hours depending upon ambient conditions

Applied Product Ready for Use

Without membrane

First Coat

: consumption : 0.3 kg/m2

Subsequent Coats: consumption : 0.3 kg/m2
Application steps

SUBSTRATE PREPARATION

Surface must be clean, sound and properly cured. Remove all loose materials mechanically, preferably with a wire brush. Iron and steel surfaces should be free of rust.

APPLICATION

For Wall (Without Membrane):

  • For porous substrate, apply first coat diluted with 10% water as primer layer. Allow enough drying time (>3 hours).
  • Apply SikaCoat Plus in two coats (0.3 kg/m2/coat), by brush or roller.

For Detailing Area (With Membrane):

  • For porous substrate, apply first coat diluted with 10% water as primer layer. Allow enough drying time (>3 hours).
  • Apply a first coat (0.8 - 1 kg/m2) of SikaCoat Plus by brush or roller.
  • Embed the SikaCoat Plus membrane into the second coat while it is still wet. Ensure that the membrane is thoroughly embedded and smooth out all air pockets and creases. Overlaps of adjacent membrane must be a minimum of 50 mm.
  • Immediately apply a second coat (0.8 - 1 kg/m2) of SikaCoat Plus while the first coat is still wet, to fully saturate the membrane from both sides.
  • When dry, apply a final top coat (~0.4 kg/m2) to complete the application. Protect from rain until dry.

CLEANING OF TOOLS

Remove uncured surface SikaCoat® Plus with water. Cured material can only be removed mechanically.