SikaGrout®-214 TD

SHRINKAGE COMPENSATED, HIGH EARLY STRENGTH, CEMENTITIOUS GROUT

SikaGrout®-214 TD is a ready to use, shrinkage compensated, non ferrous, high early strength, selflevelling, bearing grout. Pre-mixed and selectively graded materials result in a dense homogeneous mix.

  • Excellent flowability
  • Good dimensional stability
  • Controlled expansion
  • Chlorides-free; will not rust, bleed, or harm metal on contact
  • High early compressive strength; allows earlier loading and minimizes costs
  • High early strength produces minimal downtime for maintenance and repairs
  • Non toxic, non corrosive
  • Ready and easy to use
  • Economical
Product Data Sheet Show all documents

Usage

SikaGrout®-214 TD is designed to counteract the normal shrinkage of mortar and concrete and to absorb and minimize effects of vibration on foundations. It is also suitable to inject the grout in filling the gap of column’s head in top-down construction method. The high early strength property is suitable for work that requires early loads including machine bases structural columns, prestressed girders, bridge bearings, rail posts and seatings bolts etc.  

Advantages

  • Excellent flowability
  • Good dimensional stability
  • Controlled expansion
  • Chlorides-free; will not rust, bleed, or harm metal on contact
  • High early compressive strength; allows earlier loading and minimizes costs
  • High early strength produces minimal downtime for maintenance and repairs
  • Non toxic, non corrosive
  • Ready and easy to use
  • Economical

Packaging

25 kg/bag

Colour

Power / Concrete grey

Product Details

Sustainability / Certifications / Approvals

APPROVALS / STANDARDS

Local test report is available
Product Information

Shelf life

6 months from date of production if stored properly in unopened, original packaging

Storage conditions

Dry, cool, shaded place

Bulk Density

~1.6 kg/l
Technical Information

Compressive Strength

1 day

≥ 24.5 N/mm2

3 days≥ 35.0 N/mm2
7 days≥ 52.5 N/mm2

28 days

≥ 70.0 N/mm2

Expansion

≥ 0.1%

(ASTM C940)

At 27°C / 65% r.h (3 hours)

 

Application

Application Information

Mixing ratio

About 3.50 – 3.75 litres of clean water per 25 kg bag
Water content: ~14 – 15% by weight of grout powder

Fresh mortar density

~2.2 kg/l

Layer Thickness

Min. gap: 10 mm
Max. gap: Please contact Sika Technical Service Department

Flowability

≥200 mm(TCVN 9204: 2012)

With mixing ratio of 15% and at conditions of 27°C and 65 % r.h

Substrate Temperature

10°C min. / 40°C max.

Setting Time

Initial setting time≥ 3 h
Final setting time≤ 9 h
Consumption

Yield

1 bag yields approx. 13 L of mortar
Approx. 77 bags required for 1 (one) m³ of mortar
Application steps

MIXING

Powder should be added to the pre-gauged water to suit the desired consistency.
Mix mechanically for at least 3 minutes with a low speed electric drill (max. 500 r.p.m.) with a disc agitator attached, until a smooth consistency is achieved.
Mixing equipment such as two arms, forced action basket/pan type mixer can also be used

APPLICATION

Pour mortar after mixing. Ensure that air entrained into the grout is allowed to escape. When carrying out base plate grouting, ensure sufficient pressure head is maintained to keep mortar flow uninterrupted. Make sure that necessary form work is firmly in place and watertight. To achieve optimum expansion result,
apply mortar as quickly as possible.

  
Grouting of machine beds
Pre-wet thoroughly, no standing water in bolt holes. If possible, grout anchor first, and the mortar bed in the second operation. Ensure continuous flow of mortar.

  
Grouting base plate
Prewetting for approx. 24 hours, no standing water. Maintain constant hydro-static pressure to continuous flow. Use steel rods or chain to make sure that all cavities are filled. Make sure that entrapped air can escape easily.

  
Grouting of large cavities / large volume
Please contact Sika Technical Service Department for further advice.

CURING TREATMENT

Keep visible, free mortar surface as small as possible and protect it from premature drying out by standard curing practice (keep moist, cover with wet hessian, use of curing compound e.g. Antisol® E).

CLEANING OF TOOLS

Clean all tools and equipment with water immediately after use. Hardened mortar can only be removed mechanically.