Sikafloor® MultiDur ES-05 AP
SELF-SMOOTHENING FLOORING SYSTEM
Sikafloor® MultiDur ES-05 AP is a 0.5 mm self-smoothening, coloured, rigid flooring system based on epoxy resins
- Good chemical and mechanical resistance
- Good wear & abrasion resistant
- Easy application
- Liquid proof
- Gloss finish
- Easy cleanability
- Wide range of RAL colours
Usage
Sikafloor® MultiDur ES-05 AP is used as:- Self-smoothening topping for concrete and cement screeds with normal upto medium heavy wear e.g. Production area, storage and assembly halls, maintenance workshops, garages and loading ramps.
Advantages
- Good chemical and mechanical resistance
- Good wear & abrasion resistant
- Easy application
- Liquid proof
- Gloss finish
- Easy cleanability
- Wide range of RAL colours
Packaging
Please refer to the individual Product Data Sheet
Product Details
Shelf life
Please refer to the individual Product Data Sheet
Storage conditions
Please refer to the individual Product Data Sheet
Solid content by volume
100%
System Structure
Layer | Builld-up | Product |
1 | Primer | Sikafloor®-161/161 HC |
2 | Self-smoothening topping | Sikafloor®-264/264 HC |
Shore D Hardness
~ 76 (7 days / +23°C) | (DIN 53505) |
Abrasion Resistance
~ 60 mg (CS 10/1000/1000) (8 days / +23°C) | (ASTM D 4060) |
Compressive Strength
~ 53 N/mm2 (28 days / +23°C) | (EN 196-1) |
Tensile Strength in Flexure
~ 20 N/mm2 (28 days / +23°C) | (EN 196-1) |
Tensile Adhesion Strength
>1.5 N/mm² (failure in concrete) | (ISO 4624) |
CHEMICAL RESISTANCE
Resistant to many chemicals. Contact Sika technical service for specific information.
Application
Product Temperature
Please refer to the individual Product Data Sheet
Ambient Air Temperature
+8°C min. / +35°C max.
Relative Air Humidity
80 % r.h. max.
Dew Point
Beware of condensation!
The substrate must be at least 3˚C above the Dew Point to reduce the risk of condensation, which may lead to adhesion failure or “blushing” on the floor finish. Be aware that the substrate temperature may be lower than the ambient temperature.
Substrate Temperature
+8°C min. / +35°C max.
Substrate Moisture Content
Moisture content of concrete substrate must be ≤ 4% by mass (pbw – part by weight) as measured with a Tramex® CME/CMExpert type concrete moisture meter on mechanically prepared surface according to this product data sheet (preparation to CSP-3 to CSP-4 as per ICRI guidelines). Do not apply to concrete substrate with moisture levels > 4% mass (pbw – part by weight) as measured with Tramex® CME/CMExpert type concrete moisture meter. If moisture content of concrete substrate is > 4% by mass (pbw – part by weight) as measured with Tramex® CME/CMExpert type concrete moisture meter, use Sikafloor 81 EpoCem.
Pot Life
Temperature | Time |
+10°C | 50 minutes |
+20°C | 25 minutes |
+30°C | 15 minutes |
Waiting Time / Overcoating
Before applying Sikafloor®-264/264 HC on Sikafloor®-161/161 HC allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 24 hours | 3 days |
+20 °C | 12 hours | 2 days |
+30 °C | 8 hours | 1 day |
Before applying Sikafloor®-264/264 HC on Sikafloor®-264/264 HC allow:
Substrate temperature | Minimum | Maximum |
+10 °C | 30 hours | 3 days |
+20 °C | 24 hours | 2 days |
+30 °C | 16 hours | 1 day |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | ~ 72 hours | ~ 6 days | ~ 10 days |
+20°C | ~ 24 hours | ~ 4 days | ~ 7 days |
+30°C | ~ 18 hours | ~ 2 days | ~ 5 days |
Note: Times are approximate and will be affected by changing ambient conditions.
Consumption
Build-up | Product | Consumption |
Primer | Sikafloor®-161/161 HC | 0.35-0.50 kg/m² |
0.5 mm self smoothening topping | Sikafloor®-264/264 HC | 0.70 kg/m² |
SUBSTRATE QUALITY
- The concrete substrate must be sound and of sufficient compressive strength (minimum 25 N/mm2) with a minimum pull off strength of 1.5 N/mm2.
- The substrate must be clean, dry and free of all contaminants such as dirt, oil, grease, coatings and surface treatments, etc. If in doubt apply a test area first.
- Weak concrete must be removed and surface defects such as blowholes and voids must be fully exposed.
- Repairs to the substrate, filling of blowholes/voids and surface levelling can be carried out using appropriate products from the Sikafloor®, Sikadur® and Sikagard ® range of materials.
- The concrete or screed substrate has to be primed or levelled in order to achieve an even surface.
SUBSTRATE PREPARATION
- Concrete substrates must be prepared mechanically using abrasive blast cleaning or scarifying equipment to remove cement laitance and achieve an open textured surface.
- High spots must be removed by e.g. diamond grinding. All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum
MIXING
Pre - mix is recommended for component A & colour component one day prior to application. Prior to mixing, stir part A mechanically when all of part B has been added to part A, mix continuously for 2-3 minutes until a uniform mix has been achieved. De-can whole mixed materials to another container & mix for a further 1 minute to achieve consistent mix & avoid any lumps or unmixed particle in the container. Over mixing must be avoided to minimize air entrainment.
MIXING TOOLS
Sikafloor®-264 HC must be thoroughly mixed using a low speed electric stirrer (300 - 400 rpm) or other suitable equipment. For the preparation of mortars use a forced action mixer of rotating pan, paddle or trough type. Free fall mixers should not be used.
APPLICATION
Prior to application, confirm substrate moisture content, relative air humidity and dew point. If > 4 % pbw moisture content, Sikafloor® EpoCem® may be applied as a T.M.B. (temporary moisture barrier) system.
Primer
Make sure that a continuous, pore free coat covers the substrate. If necessary, apply two priming coats. Apply Sikafloor®-161/161 HC by brush, roller or squeegee. Preferred application is by using a squeegee and then back rolling crosswise.
Levelling
Rough surfaces need to be levelled first. Therefore use e.g. Sikafloor®-161/161 HC levelling mortar (see PDS).
Self smoothening
Sikafloor®-264/264 HC as self smoothening topping can be applied by pin rack, notch trowel back roll with spikeroller crosswise.
CLEANING OF TOOLS
Clean all tools and application equipment with suitable solvent immediately after use. Hardened and/or cured material can only be removed mechanically.