Sikafloor® MultiDur EB-10 AP
BROADCAST EPOXY FLOOR COVERING WITH HIGH MECHANICAL RESISTANCE
Sikafloor® MultiDur EB-10 AP is a slip resistant, coloured, rigid flooring system based on epoxy resins with high mechanical resistance.
- Good chemical and mechanical resistance
- Good wear & abrasion resistant
- Good slip resistance
- Easy application
- Liquid proof
- Wide range of RAL colour
System Structure
1
Primer and seal coat
Usage
Sikafloor® MultiDur EB-10 AP is used as:- Broadcast systems for multistorey and underground car parks, maintenance hangars and wet process areas of beverage and food industry.
- Broadcast systems for applications where slip resistance is desired.
Advantages
- Good chemical and mechanical resistance
- Good wear & abrasion resistant
- Good slip resistance
- Easy application
- Liquid proof
- Wide range of RAL colour
Packaging
Please refer to the individual Product Data Sheet
Colour
Available in RAL shades
Appearance
Antiskid finish
System Details
System Structure
Layer | System | Product |
1 | Base/ receiver coat + Broadcast | Sikafloor®-264/264 HC + Quartz sand(0.4-0.6mm) |
2 | Seal coat | Sikafloor®-264/264 HC |
Chemical base
Epoxy
Minimum Thickness
1 mm
Shelf life
Please refer to the individual Product Data Sheet
Storage conditions
Please refer to the individual Product Data Sheet
Shore D Hardness
76 (7 days / +23°C) | (DIN 53505) |
Abrasion Resistance
60 mg (CS 10/1000/1000) (8 days / +23°C) | (ASTM D 4060) |
Compressive Strength
53 N/mm2 (28 days / +23°C) | (EN196-1) |
Tensile Strength in Flexure
20 N/mm2 (28 days / +23°C) | (EN 196-1) |
CHEMICAL RESISTANCE
Resistant to many chemicals. Contact Sika Technical Service for specific information.
Application
Product Temperature
Please refer to the individual Product Data Sheet
Ambient Air Temperature
+8 °C min. / +35 °C max.
Relative Air Humidity
80% max.
Dew Point
Beware of condensation!
The substrate must be at least 3˚C above the Dew Point to reduce the risk of condensation, which may lead to adhesion failure or “blushing” on the floor finish. Be aware that the substrate temperature may be lower than the ambient temperature.
Substrate Temperature
+8 °C min. / +35 °C max.
Substrate Moisture Content
Moisture content of concrete substrate must be ≤ 4% by mass (pbw – part by weight) as measured with a Tramex® CME/CMExpert type concrete moisture meter on mechanically prepared surface according to this product data sheet (preparation to CSP-3 to CSP-4 as per ICRI guidelines). Do not apply to concrete substrate with moisture levels > 4% mass (pbw – part by weight) as measured with Tramex® CME/CMExpert type concrete moisture meter. If moisture content of concrete substrate is > 4% by mass (pbw – part by weight) as measured with Tramex® CME/CMExpert type concrete moisture meter, use Sikafloor®-81 EpoCem®.
Pot Life
Temperature | Time |
+10°C | 50 minutes |
+20°C | 25 minutes |
+30°C | 15 minutes |
Waiting Time / Overcoating
Before applying Sikafloor®-264/264 HC 2nd coat on Sikafloor®-264/264 HC allow:
Substrate temperature | Minimum | Maximum |
+10°C | 30 hours | 3 days |
+20°C | 24 hours | 2 days |
+30°C | 16 hours | 1 day |
Times are approximate and will be affected by changing ambient conditions particularly temperature and relative humidity.
Applied Product Ready for Use
Temperature | Foot traffic | Light traffic | Full cure |
+10°C | 72 hours | 6 days | 10 days |
+20°C | 24 hours | 4 days | 7 days |
+30°C | 18 hours | 2 days | 5 days |
Note: Times are approximate and will be affected by changing ambient conditions
Consumption
System | Product | Consumption |
Base/receiver coat | Sikafloor®-264/264 HC | 0.40 kg/m² |
Broad cast in excess | Quartz sand (0.4-0.6mm) | 2.0 kg/m² |
Sealer coat | Sikafloor®-264/264 HC | 0.6 kg/m² |
EQUIPMENT
Sikafloor®-264/264 HC must be thoroughly mixed using a low speed electric stirrer (300 - 400 rpm) or other suitable equipment. For the preparation of mortars use a forced action mixer of rotating pan, paddle or trough type. Free fall mixers should not be used.
SUBSTRATE QUALITY
- The concrete substrate must be sound and of sufficient compressive strength (minimum 25 N/mm2) with a minimum pull off strength of 1.5 N/mm2.
- The substrate must be clean, dry and free of all contaminants such as dirt, oil, grease, coatings and surface treatments, etc. If in doubt apply a test area first.
- Weak concrete must be removed and surface defects such as blowholes and voids must be fully exposed.
- Repairs to the substrate, filling of blowholes/voids and surface levelling can be carried out using appropriate products from the Sikafloor®, Sikadur® and Sikagard® range of materials.
- The concrete or screed substrate has to be primed or levelled in order to achieve an even surface.
SUBSTRATE PREPARATION
Concrete substrates must be prepared mechanically using abrasive blast cleaning or scarifying equipment to remove cement laitance and achieve an open textured surface.
High spots must be removed by e.g. diamond grinding. All dust, loose and friable material must be completely removed from all surfaces before application of the product, preferably by brush and/or vacuum
MIXING
Pre - mix is recommended for component A & colour component one day prior to application. Prior to mixing, stir part A mechanically when all of part B has been added to part A, mix continuously for 2-3 minutes until a uniform mix has been achieved. De-can whole mixed materials to another container & mix for a further 1 minute to achieve consistent mix & avoid any lumps or unmixed particle in the container. Over mixing must be avoided to minimize air entrainment.
APPLICATION
Prior to application, confirm substrate moisture content, relative air humidity and dew point. If > 4 % pbw moisture content, Sikafloor® EpoCem® may be applied as a T.M.B. (temporary moisture barrier) system.
Base/receiver coat
Make sure that a continuous, pore free coat covers the substrate. Sikafloor®-264/264 HC by trowel & back roll with spike roller.
Broad cast:
Broad cast quartz sand in as per consumption uniformly on base layer
Sealcoating
Sikafloor®-264/264 HC seal coat can be applied by sqeezee & back roll with coating roller.
CLEANING OF TOOLS
Clean all tools and application equipment with Thinner C or suitable solvent immediately after use. Hardened and/or cured material can only be removed mechanically.
CLEANING
To maintain the appearance of the floor after application, Sikafloor®-264 HC broadcast finish surface must have all spillages removed immediately and must be regularly cleaned using rotary brush, mechanical scrubbers, scrubber dryer, high pressure washer, wash and vacuum techniques etc. using suitable detergents and waxes. Refer to the document "Cleaning & Maintenance guideline"